Page:United States Statutes at Large Volume 116 Part 4.djvu/784

 116 STAT. 3212 PROCLAMATION 7529-MAR. 5, 2002 ANNEX (continued) 23 (xlvii) wire rod products known as "DSUS 70DH wire rod" and designated as X-177, the foregoing of stainless steel, having the following chemical composition (in percent by weight) carbon 0.60 - 0.70; silicon maximum 0.35; manganese 0.60 - 0.80; phosphorus maximum 0.30; sulfur maximum 0.010; chromium 12.50 - 13.50; with a delivered hardness of HRB 99 maximum and hardness after heat treatment of HRC minimum 58 (quenching 1050 "C for 20 - 30 minutes AC, sub-zero -73 "C for I HR, leinpcring ISO "C for I Hr AC), (xl\ iii) welded pipes and tubes designated as X-066, X-069, X-079, X-071, X-102, X-139 or X-1S2. as described below: (A) products having an outside diameter measuring 457.2 mm or more but not more than 558.8 mm, with a wall thickness measuring 19.05 mm or more, regardless of grade; (B) products having an outside diameter measuring 609.6 mm or more but less than 914.4 mm, the foregoing with a wall thickness measuring over 22.3 mm in grades A, B and X42; a wall thickness measuring over 19.05 mm in grades X52 through X5; or a wall thickness measuring over 17.48 mm in grade X60 or higher; (C) products having an outside diameter measuring 762 mm or more but less than 914.4 mm, the foregoing with a wall thickness measuring over 31.75 mm in grades A, B and X42; a wall thickness measuring over 25 4 mm in grades X52 through X56; or a wall thickness measuring over 22.3 mm in grades X60 or higher; (D) products having an outside diameter measuring 914.4 mm or more but less than 1066.8 mm, the foregoing with a wall thickness measuring over 34.93 mm in grades A, B and X42; a wall thickness measuring over 31.75 mm in grades X52 through X56; or a wall thickness measuring over 28.58 mm in grades X60 or greater; (E) products having an outside diameter nieasuringl066.8 mm or more but less than 1625.6 mm, the foregoing with a wall thickness measuring over 38.1 mm in grades A, B and X42; a wall thickness measuring over 34.93 mm in grades X52 through X56, or a wall thickness measuring over 31.75 mm in grades X60 or higher; (F) products having an outside diameter measuring 1219.2 to 1320.8 mm, inclusive, with a wall thickness measuring 20.57 mm or more in grades X-80 or higher; or (G) products having an outside diameter measuring 1219.2 to 1320.8 mm, inclusive, with a wall thickness of 13.72 mm or more in grades X-IOO or higher; or (xlix) welded pipe and tube products designated as X-132, which are DOM tubing for electric submersible oil pump motors; with outside diameters of 95.25 mm to 171.83 mm, inclusive; having the following chemical composition (in percent by weight): carbon maximum 0.15; silicon 0.25 - 1.00, inclusive; manganese 0.30 - 0.60, inclusive; phosphorus maximum 0.030; sulfur maximum 0.030; chromium 8.00 - 10.00. inclusive, molybdenum 0.90 - 1.10, inclusive. (c) Goods may also be excluded from the application of relief if they are covered by a determination by the United States Trade Representative (USTR) published in the Federal Register by not later than July 3, 2002, or in March of any subsequent year in which this note remains in effect, that such goods should be exempt from the application of any rate of duty or tariff-rate quota otherwise imposed on goods described in the applicable superior text. Such a determination by the USTR under this subdivision may exempt specific additional steel products when entered from all countries or when entered from enumerated countries only, or may modify the product descriptions in subdivision (b) of this note. The USTR is authorized to modify or terminate any such determination during the effective period of the subheadings specified in the first sentence of subdivision (a) of this note and to specify, subsequent to the effective date specified in this note, that such stool products will be considered "goods excluded from the application of relier upon publication by tho USTR of a notice in the Federal Reuistcr. Such "goods excluded from the application of relief shall not be counted toward any tariff-rate quota quantities specified for any quota period. (d)(i) For the purposes of this note and the application of subheadings 9903.72.30 through 9903.74.24,

�