Page:United States Statutes at Large Volume 116 Part 4.djvu/777

 PROCLAMATION 7529-MAR. 5, 2002 116 STAT. 3205 ANNEX (continued) 16 0.80 percent by weight, manganese maximum 1.80 percent by weight, phosphorus maximum 0.015 percent by weight, silicon maximum 0.010 percent by weight; (II) product 2: thickness 0.8 mm - less than 1.0 mm; minimum tensile strength 780 N/mm-; yield strength 410 N/mm' - 635 N/mm'; elongation 15-26 percent; chemical composition: carbon maximum 0.10 percent by weight, silicon maximum 0 80 percent by ucighl, nungancsc nia.ximum 1.80 percent by ucighl, phosphorus maximum 0.015 percent by weight, silicon maximum 0.010 percent by weight; (III) product 3: thickness 1.0 mm - less than 1.2 mm; minimum tensile strength 780 N/mnv"; yield strength 400 - 625 N/mm-; elongation 16- 27 percent; chemical composition; carbon maximum 0.10 percent by weight, silicon maximum 0,80 percent by weight, manganese maximum 1.80 percent by weight, phosphorus maximum 0.015 percent by weight, silicon maximum 0.010 percent by weight; (IV) product 4: thickness I 2 mm - less than 1.6 mm; minimum tensile strength 780 N/mm-; yield strength 400 - 625 N/mm*, elongation 15-28 percent; chemical composition; carbon maximum 0.10 percent by weight, silicon maximum 0.80 percent by weight, manganese maximum 1.80 percent by weight, phosphorus maximum 0 015 percent by weight, silicon maximum 0.010 percent by weight; (V) product 5; thickness 1.6 mm - 2.3 mm; minimum tensile strength 780 N/mm-; yield strength 400 - 625 N/mm'; elongation minimum 18 percent; chemical composition; carbon maximum 0.10 percent by weight, silicon maximum 0.80 percent by weight, manganese maximum 1.80 percent by weight, phosphorus maximum 0 015 percent by weight, silicon maximum 0.010 percent by weight. (VI) product 6; thickness 0.8 mm - less than 1.0 mm; minimum tensile strength 1180 N/mm-; yield strength 835 - 1225 N/mm'; elongation 5-10 percent; chemical composition; carbon maximum 0.15 percent by weight; silicon maximum 0.80 percent by weight; manganese maximum 2.00 percent by weight; phosphorus maximum 0.010 percent by weight; silicon maximum 0.010 percent by weight; (VII) product 7; thickness 1.0 mm - less than 1.2 mm; minimum tensile strength 1180 N/mm-; yield strength 825 - 1215 N/mm-; elongation 6-17 percent; chemical composition: carbon maximum 0.15 percent by weight; silicon maximum 0.80 percent by weight; manganese maximum 2.00 percent by weight; phosphorus maximum 0.010 percent by weight; silicon maximum 0.010 f)ercent by weight, (VIII) product 8; thickness 1.2 mm - less than 1.6 mm; minimum tensile strength 1180 N/mm-; yield strength 825 - 1215 N/mm^ elongation 7-18 percent; chemical composition: carbon maximum 0.15 percent by weight; silicon maximum 0.80 percent by weight; manganese maximum 2.00 percent by weight; phosphorus maximum 0.010 percent by weight; silicon maximum 0.010 percent by weight; (IX) product 9; thickness 1.6 mm - 2.3 mm; minimum tensile strength 1180 N/mnr; yield strength 825 - 1215 N/mm-; elongation minimum 8 percent; chemical composition; carbon maximum 0.15 percent by weight; silicon maximum 0.80 percent by weight; manganese maximum 2.00 percent by weight; phosphorus maximum 0.010 percent by weight; silicon maximum 0.010 percent by weight; (X) product 10; thickness 1.0 mm- less than 1.2 mm; minimum tensile strength 1270 N/mm^ yield strength 980 - 1270 N/mm'; elongation 6- 17percent; chemical composition: carbon maximum 0.15 percent by weight; silicon maximum 0.80 percent by weight; manganese maximum 2.00 percent by weight; phosphorus maximum 0.010 percent by weight; silicon maximum 0.010 percent by weight; (XI) product 11: thickness 1.2 mm - less than 1.6 mm; minimum tensile strength 1270

�