Page:United States Statutes at Large Volume 116 Part 4.djvu/771

 PROCLAMATION 7529-MAR. 5, 2002 116 STAT. 3199 ANNEX (continued) 10 (x\ i) horrollcd products designated as X-046, as described below: (A) products known as "Domex 110," not further processed than hot rolled, in thicknesses of between 4.55 and 111 mm, inclusive, and widths of between 889 and 1600 mm, inclusive, containing, by weight, carbon of 0.12 percent maximum, silicon of 0.60 percent maximum, manganese of 2.0 percent maximum, phosphorus of 0.025 percent maximum, sulphur of 0.010 percent maximum, aluminum of at least 0.015 percent, columbium of 0.09 percent maximum and titanium of 0.20 percent maximum; exhibiting yield strength of 758 MPa, tensile strength of 813 MPa, elongation of 15 percent, bendability of 1.6 to l.Sxt, and impact toughness of 27 J at -40- C (provided for in subheading 7208.36.00, 7208.37.00, 7208.38.00, 7208.39.00, 7225.30.30 or 7225.30.70), the foregoing also designated as X-108; or (B) products known as "Domex Wear," not further processed than hot rolled, in thicknesses of between 3.00 and 6.35 mm, inclusive, and widths of between 889 and 1600 mm, inclusive; containing, by weight, carbon of 0.17 percent typical value (TV), silicon of 0.30 percent TV, manganese of 1.8 percent TV, phosphorus of 0.01 percent TV, sulphur of 0.010 percent maximum, chromium of 0.3 percent TV, molybdenum of 0.10 percent TV, aluminum of 0.04 percent TV and titanium of 0.16 percent TV; exhibiting yield strength of 793 MPa, tensile strength of 931 MPa, elongation of 15 jjercent, bendability of 2xt and impact toughness of 27 J at -40* C (provided for in subheading 7208.36.00, 7208.37.00, 7208.38.00, 7208.39.00, 7225.30.30 or 7225.30.70), the foregoing also designated as X-108; (xvii) hot-rolled transformation-Induced plasticity (TRIP) steel designated as X-061, as described below: (A) TRIP steel, Variety 1. not further worked than hot-rolled, with the following chemical composition, by weight: carbon, up to 0.21 percent; silicon, up to 2.2 percent; manganese, up to 1.8 percent; phosphorus, up to 0.025 percent; sulfur, up to 0.01 percent; physical and mechanical properties: thickness from 1.4 to 6.0 mm (inclusive); minimum yield point (MPa) of 390; minimum tensile strength (MPa) of 590; minimum elongation of 25 percent if 1400 mm to 1999 mm thickness range; minimum elongation of 26 percent If 2000 mm to 2499 mm thickness range; minimum elongation of 27 percent if 2500 mm to 3249 mm thickness range; minimum elongation of 28 percent if 3250 mm to 3999 mm thickness range; or minimum elongation of 28 percent if 4000 mm to 6000 mm thickness range; (B) TRIP steel, Variety 2, not further worked than hot-rolled, with the following chemical ' composition, by weight: cartron, up to 0.23 percent, silicon, up to 2.2 percent, manganese, up to 2.0 percent; phosphorus, up to 0.025 percent; sulfur, up to 0.01 percent; physical and mechanical properties: thickness range from 1.4 to 6.0 mm (inclusive); minimum yield point (MPa) of 440; minimum tensile strength (MPa) of 690; minimum elongation of 22 percent if 1400 mm to 1999 mm thickness range; minimum elongation of 23 percent if 2000 mm to 2499 mm thickness range; minimum elongation of 24 percent if 2500 mm to 3249 mm thickness range; minimum elongation of 25 percent if 3250 mm to 3999 mm thickness range; or minimum elongation of 26 percent if 4000 mm to 6000 mm thickness range; (C) TRIP steel, Variety 3, not further worked than hot-rolled, with the following chemical composition, by weight: carbon, up to 0.25 percent; silicon, up to 2.2 percent; manganese, up to 2.2 percent; phosphorus, up to 0.025 percent; sulfur, up to 0.01 percent; physical and mechanical propenies: thickness range from 1.4 to 6.0 mm (inclusive); minimum yield point (MPa) of 490; minimum tensile strength (MPa) of 780; minimum elongation of 20 percent if 1400 mm to 1999 mm thickness range; minimum elongation of 21 percent if 2000 mm to 2499 mm thickness range; minimum elongation of 22 percent if 2500 mm to 3249 mm thickness range; minimum elongation of 23 percent if 3250 mm to 3999 mmthickness range; or minimum elongation of 24 percent if 4000 mm to 6000 mm thickness range;or

�